Sulfurized polyisobutylene based wear and oxidation inhibitors

ABSTRACT

Sulfurized olefin compositions and components are prepared from sulfurizing high methylvinylidene polyisobutylene(s) having at least 25% methylvinylidene and a number average molecular weight in the range of about 120 to about 600, at suitable temperatures and pressures. The resulting sulfurized reaction product and polyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds and derivatives are useful in lubricating oils.

FIELD OF THE INVENTION

[0001] This invention is directed in part to sulfurized olefincompositions and components prepared by sulfurizing polyisobutylene(s)containing a high concentration of the methyl vinylidene isomer (highlyreactive polyisobutene, HR PIB), at suitable temperatures and to theresulting reaction products, including thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds andderivatives thereof. This invention also discloses of the process toprepare the sulfurized polyisobutyl reaction products, the use of suchcompounds, and lubricant compositions containing them as well asenriched compositions containingpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds andderivatives.

BACKGROUND OF THE INVENTION

[0002] Sulfurized olefins, e.g. sulfurized isobutylene and lubricantcompositions containing such sulfurized isobutylene, are well known inthe art as lubricant additives imparting extreme pressure and antiwearcapabilities.

[0003] The metal surfaces of machinery or engines operating under heavyloads, wherein metal slides against metal, may undergo excessive wear orcorrosion. Often the lubricants used to protect the metal surfacesdeteriorate under such heavy loads and as a result, do not prevent wearat the points of metal to metal contact. Consequently, the performanceof the machine or engine will suffer, and in aggravated cases themachine or engine may become completely inoperative. While sulfurizedolefins have shown some benefit when added as lubricant additive, inmany instances their application is limited since some types ofsulfurized olefins have: an undesirable corrosion property (especiallytowards copper), generate malodorous by-products in operation, and/orhave stability and compatibility issues.

[0004] Sulfurized olefins have been extensively used in many lubricantapplications requiring extreme pressure/antiwear activity. Thesesulfurized olefins which include sulfurized C₃-C₈ olefins such asisobutylene are described by U.S. Pat. Nos. 3,703,504; 3,703,505; and3,873,454. These patents and U.S. Pat. No. 4,240,958 generally employmethods of preparing their sulfurized products wherein the olefin issulfohalogenated with a sulfur halide at some stage in their synthesis.

[0005] Sulfurized olefins have also been prepared by the directsulfurization of olefins with sulfur and hydrogen sulfide, see U.S. Pat.Nos. 2,337,473; 4,119,549; 4,119,550; 4,191,659; 4,344,854 and4,147,640. U.S. Pat. No. 4,147,640, for example, describes thesulfurization of various olefinic hydrocarbons such as dicyclopentadienewith sulfur and hydrogen sulfide. Also disclosed are methods ofpreparing sulfurized compounds by contacting an olefinic feedstock withsulfur and hydrogen. The olefin can be isobutene and the catalyst can beammonia or an amine, typically these products are alkyl-alkenylpolysulfide mixtures and polymeric polysulfides.

[0006] The direct sulfurization of olefins such as diisobutylene andtriisobutylene with sulfur is described, for example, in U.S. Pat. Nos.2,995,569 and 3,796,661. When triisobutylene is employed, these patentsdescribe the formation of exclusively 4-neopentyl-5-tertiarybutyl-1,2-dithiole-4-cyclopentene-3-thione with a minor amount oforganic sulfides and polysulfides. The direct sulfurization processemployed elevated temperatures at both low and elevated pressures. U.S.Pat. No. 3,697,221 discloses of several 1,2-dithiole-3-thionederivatives as intermediates to the thionium methosulfates. U.S. Pat.No. 4,042,514 discloses of alkylthio and alkylarylthio derivatives of1,2-dithiole-3-thiones. U.S. Pat. No. 4,194,980 discloses cyclicsulfurized olefins prepared by reacting an olefin with a cyclicpolydisulfide. U.S. Pat. Nos. 3,345,380, 2,535,706, 2,535,705 describemethods of making various thiones by reacting elemental sulfur andisobutylene and other unsaturated hydrocarbons. U.S. Pat. No. 3,364,232discloses high molecular weight trithiones prepared by reacting anolefin of at least 30 carbons in the presence of sulfur and asubstituted trithione.

[0007] Thus, it is well known that many methods have been used forproducing organic sulfides by treating olefins. It is also well knownthat many sulfurized organic compositions are useful as lubricantadditives. Some of the prior art teaches that thiones are undesirableespecially high levels of thiones, such as dithiol-thiones (ordithiolethiones), or high levels of thiones in combination with variouscomplex sulfurized mixtures. Typically these thiones need to be removed.Dithiolethione-free sulfurized olefin compositions have been prepared bythe reaction of sulfur, isobutylene and hydrogen sulfide as exemplifiedby U.S. Pat. No. 4,344,854 noted above, or U.S. Pat. No. 5,135,670 alsoemploying a sodium sulfate nonahydrate, and for example U.S. Pat. No.5,338,468 employing elemental sulfur, isobutylene and an amine base.U.S. Pat. No. 5,849,677 discloses extraction of4-methyl-3H-1,2-dithiole-3-thione (“MDTT”) from a sulfurized olefin feedstream using solvent extraction.

[0008] It has now been discovered that the reaction of sulfur and ahighly reactive methylvinylidene polyisobutylene produces a low odor,sulfurized polyisobutylene reaction product having anti-wear, extremepressure load capacity, and antioxidant characteristics; which issuitable for use, for example, as a lubricant additive. Such reactionproduct and resulting polyisobutyl-1,2-dithiole-4-cyclopentene-3-thionesreaction products are thermally more stable relative to the conventionalsulfurized isobutylene, do not have a strong odor, and are anticipatedto be more stable in the presence of acids. Accordingly, there is a needfor methods to prepare and use these reaction products, to thecomponents themselves as well as mixtures thereof, and to compositionsemploying them.

SUMMARY OF THE INVENTION

[0009] This invention relates to sulfurized olefin compositions preparedfrom sulfurizing high methylvinylidene polyisobutylene(s) “HR PIB” atsuitable reaction temperatures and to the resulting sulfurized productand resulting polyisobutyl-1,2-dithiole-4-cyclopentene-3-thionecompounds “PDCT” produced therefrom, including the use of such compoundsand/or compositions, and lubricant compositions containing them as wellas derivatives thereof. More specifically, the compositions andcompounds of the present invention are prepared by sulfurization of ahighly reactive polyisobutylene having at least 25% of amethylvinylidene isomer and wherein the polyisobutylene has a numberaverage molecular weight in the range of about 120 to about 600 with asulfur source at a reaction temperature in excess of about 175° C.Accordingly, a process for preparing a sulfurized olefin compositioncomprising reacting polyisobutylene having at least 25% of amethylvinylidene isomer and wherein the polyisobutylene has a numberaverage molecular weight in the range of about 120 to about 600 with asulfur source at a reaction temperature in excess of about 175° C. isdisclosed. In either event, a preferred polyisobutylene having a2-methylvinylidene content in the amount of at least 25% with an averagemolecular weight in the range of 120 to 600. One such suitablepolyisobutylene feedstream is generated as by-product in typicalcommercial highly reactive polyisobutylene production, which heretoforhad little economic value.

[0010] In a preferred embodiment, the polyisobutylene moiety is selectedfrom a mixture of C₈H₁₆ to C₃₂H₆₄ oligomers. And even more preferred,the polyisobutylene comprises about 5 wt. % to about 20 wt. % C₈H₁₆,about 35 wt. % to about 55 wt. % C₁₂H₂₄, about 20 wt. % to about 30 wt.% C₁₆H₃₂, about 8 wt. % to about 15 wt. % C₂₀H₄₀, about 2 wt. % to about8 wt. % C₂₄H₄₈, and about 0.5 wt. % to about 2 wt. % C₂₈H₅₆ and lessthan 2 wt% C₃₂H₆₄.

[0011] As is frequently the case with olefin sulfurization products, thereaction product is typically a mixture of products because of competingor sequential reactions which can result in secondary or derivativeproducts, such as dialky, cyclic and the polyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds, of which the latter areproduced in a major amount. In general a commercial product will be amixture of sulfurized compounds since often there is little benefit toisolate the individual compounds. However, it has been shown in someapplications further purifiedpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds demonstrateimproved results when employed in lubricating compositions. Accordinglythis invention is directed to the resultingpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compound(s) andmixtures thereof. Especially preferred are the variouspolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione isomers formed.

[0012] The principal sulfurization product and derivative thereof,referred to herein as polyisobutyl-1,2-dithiole-4-cyclopentene-3-thione,can be represented by the formula:

[0013] wherein R₁ is hydrogen or methyl; X is sulfur or oxygen; m is aninteger from 1 to 9; and

[0014] n is 0 or 1, with the condition that when n is 0 then R₁ ismethyl, and when n is 1 then

[0015] R₁ is hydrogen. Preferably X is sulfur and in one aspect, R₁ ismethyl and in another,

[0016] R₁ is hydrogen.

[0017] The present invention further provides lubricating composition(s)that are thermally stable, resistant to acid attack and are useful asextreme pressure (EP) and/or antiwear agents and/or antioxidants inlubricants, functional fluids, and normally liquid fuels. The sulfurizedhigh methylvinylidene polyisobutylene product and resultingpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds areparticularly suited for engine and gear lubricants and accordingly oneaspect is directed to lubricating compositions comprising an oil oflubricating viscosity and one or more of thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds of thisinvention. These lubricating compositions can be further formulated withadditional additives, such as dispersants, detergents, oil solublephosphorous containing compounds selected from extreme pressure agentsand antiwear agents, and alkali-metal borates. Accordingly, lubricatingcompositions can be initially formulation with thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds of thisinvention or top treated with an amount suitable for EP, antiwear orantioxidant property desired.

DETAILED DESCRIPTION OF THE INVENTION

[0018] The present invention relates to the preparation of sulfurizedolefins and other polyisobutyl-1,2-dithiole-4-cyclopentene-3-thionecompositions using a low molecular weight highly reactivepolyisobutylenes as the olefin reagent. Highly reactive polyisobutylenes(HR PIB) are valued for use in the lubricating oil additive industry andare commercially produced in the chemical industry. These valued HR PIBpolymers are characterized by the presence of significant amounts of2-methylvinylidene isomers, RC(CH₃)═CH₂ where R is a polyisobutylresidue, and a molecular weight preferably in the range of about 500 to5000. In addition to valued high molecular weight products, there existsan under utilized low molecular weight HR PIB distillate generallyregarded as a waste product. Such methylvinylidene polyisobutylenes aretypically prepared using boron trifluoride catalysis. The preparation ofsuch polyisobutylenes in which the methylvinylidene isomer comprises ahigh percentage of the total olefin composition is described in U.S.Pat. Nos. 4,152,499 and 4,605,808, the disclosures of which areincorporated herein by reference.

[0019] This invention is directed to compounds and compositions preparedby sulfurization of a highly reactive polyisobutylene having at least25% of a methylvinylidene isomer and wherein the polyisobutylene has anumber average molecular weight in the range of about 120 to about 600with a sulfur source at a reaction temperature in excess of about 175°C. One aspect of this invention is directed to low molecular weightpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compositions,compounds and derivatives represented by the formula I:

[0020] wherein R₁ is hydrogen or methyl; X is sulfur or oxygen; m is aninteger from 1 to 9; and

[0021] n is 0 or 1, with the condition that when n is 0 then R₁ ismethyl, and when n is 1 then

[0022] R₁ is hydrogen. Preferably X is sulfur and in one aspect, R₁ ismethyl and in another,

[0023] R₁ is hydrogen. Preferably, m is an integer from 1 to 6, morepreferably 1 to 5 and more preferably 2 to 5. In another aspect, m isgreater than one. Compounds of Formula I have also been referred to inthe art as pseudo-aromatic sulfur compounds, thiones, dithiol-thiones,trithiones, as well as 1,2-dithiole-3-thiones. However, as used hereinsuch compounds are referred to as 1,2-dithiole-4-cyclopentene-3-thionesand more specifically aspolyisobutyl-1,2-dithiole-4-cyclopentene-3-thiones, since they arepolyisobutyl substituted.

[0024] The compositions can also be prepared using a singlepolyisobutylene oligomer fraction such as tri-isobutylene,tetra-isobutylene, penta-isobutylene, hexa-isobutylene orhepta-isobutylene; these fractions may contain various polyisobuteneisomers including at least 25% of the methyl vinylidene isomer. Thesecompositions can be further purified to specific isomer compounds usingseparation techniques known in the art for example, distillation,solvent refining, crystallization, and the like.

[0025] Highly Reactive Polyisobutylene

[0026] It is generally known by those skilled in the art that thecommercial HR PIB production process described above generates a HR PIBdistillate byproduct that; (i) contains mostly C₈H₁₆ to C₂₈H₅₆ oligomers(average C₁₄H₂₈), (ii) exhibits a relatively low average molecularweight of about 200 and, (iii) contains 2-methylvinylidene in the amountof at least about 25%. This low molecular weight distillate byproduct,which amounts to several percent of total HR PIB production, has littlevalue and is typically sold as a fuel product. Thus, a need exists inthe chemical industry to develop a valuable use for the HR PIBdistillate byproduct. The present invention fulfills this need byproviding a process for preparation of sulfurized olefins and otherpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compositions andderivatives thereof, preferably employing the HR PIB distillatebyproduct, or fractions thereof.

[0027] For purposes of this invention, the term “polyisobutylene” refersto a HR PIB containing at least about 25% of a 2-methylvinylidene isomerand is further defined as comprising a mixture of highly reactivepolyisobutylene oligomers. In a preferred embodiment, said mixturecontains mostly C₈H₁₆ to C₂₈H₅₆ oligomers and may contain fractionalamounts of C₃₂H₆₂ oligomers (average C₁₄H₂₈), exhibiting an averagemolecular weight in the range of about 120 to about 600, preferably inthe range of 150 to about 400, and more preferably in the range of about160 to about 280 (an average of about 200). Such HR PIB useful in thisinvention may employ the HR PIB distillate byproduct. The olefinic bondsof a preferred low molecular weight HR PIB comprise at least about 25%methylvinylidene content, preferably in the range of about 25% to about95%, more preferably about 40% to about 95%, and even more preferablyabout 60% to about 90% methylvinylidene isomer. Dilsobutylene (C₈H₁₆)may be present in a fractional amounts from 0% to less than 50% basedupon weight of HR PIB.

[0028] Preferred low molecular weight HR PIBs comprise less than about32 carbon atoms, for example, one or more of: 32 carbon atoms, 28 carbonatoms, 24 carbon atoms, 20 carbon atoms, 16 carbon atoms, 12 carbonatoms, and 8 carbon atoms. More preferred low molecular weight HR PIBscomprise from about 8 to about 28 carbon atoms. Most preferred lowmolecular weight HR PIBs comprise from about 12 to about 28 carbonatoms. Preferred low molecular weight HR PIBs have a molecular weight ofabout 448 or less. More preferred low molecular weight HR PIBs have amolecular weight of about 120 to about 392. Most preferred low molecularweight HR PIB has a molecular weight of about 168 to about 392.

[0029] The HR PIBs of this invention may be mixtures of individual lowmolecular weight polyisobutylene components of varying molecularweights. A mixture of low molecular weight HR PTBs might comprise any orall of C₈, C₁₂, C₁₆, C₂₀, C₂₄, C₂₈ and C₃₂ molecules. One embodiment ofthis invention may comprise the use of low molecular weight HR PIBmolecules that have been separated according to carbon number. Forexample, a HR PIB mixture may be distilled to provide compositions thatcomprise one or more of C₈, C₁₂, C₁₆, C₂₀, C₂₄ C₂₈, or C₃₂ molecules,with the proviso that when diisobutylene is employed it is maintained ina fractional amount. Preferred low molecular weight HR P1Bs of thisinvention are those that are used as a mixture of varying molecularweights. A preferred low molecular weight HR PIB mixture may have thenumber average molecular weight (M_(n)) of about 150 to about 240 andmore preferably from about 175 to about 225.

[0030] A preferred low molecular weight HR PIB mixture may comprise thefollowing: about 5 wt. % to about 20 wt. % C₈H₁₆, about 35 wt. % toabout 55 wt. % C₁₂H₂₄, about 20 wt. % to about 30 wt. % C₁₆H₃₂, about 8wt. % to about 15 wt. % C₂₀H₄₀, about 2 wt. % to about 8 wt. % C₂₄H₄₈,and about 0.5 wt. % to about 2 wt. % C₂₈H₅₆. C₃₂H₆₄ and higher speciesmay comprise about 2 wt. % or less of the total. In a more preferredembodiment, the C₈H₁₆ are removed from the above mixture with theremaining weight percents adjusted accordingly. Preferably, the mixturescontains a high methylvinylidene content of from about 50 to 95 % ormore and more preferably from about 60-85 % methylvinylidene and havinga M_(n) of from about 175 to about 225.

[0031] There are several advantages to using the presently employedpolyisobutylene oligomers to prepare sulfurized products including thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione and derivativesthereof; for example: (1) the sulfurization reaction can be carried outat elevated temperatures under low pressure; (2) flexibility inutilizing a new, previously under utilized feedstock, which can becomprised of specific carbon number fractions, a mixture of selectedfractions or, most desirably, use of the total, unfractionated HR PIBdistillate byproduct, with or without removal of inert solvent (2% to10%); (3) the sulfurization reaction can be carried out at relativelylower temperatures, which because of the greater reactivity afforded bythe presence of 2-methylvinylidene results in a liquid product and nosolid product under reaction conditions as is usual in low temperaturereactions with conventional diisobutylene, and; (4) milder, lowtemperature reaction conditions can be employed to controlfragmentation.

[0032] Sulfur

[0033] Any suitable sulfur source can be used for the sulfurization ofthe HR PIB. Elemental sulfur, hydrogen sulfide, sulfur dioxide, sodiumsulfide hydrates are well known and are commercially available.Preferably elemental sulfur is used and which can be heated to themolten state to hasten the reaction kinetics and minimize the formationof mono- and polysulfides, dithiole derivatives including mercaptocomponents; although the latter of which can be further decomposed intothe polyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compositions ofthe present invention.

[0034] The amounts of sulfur per mole of HR PIB compound are,respectively, about 1.0-3.5 gram-atoms and about 0.1-1.5 moles. Thepreferred ranges are about 2.0-3.1 gram-atoms and about 0.4-1.25 molesrespectively, and the most desirable ranges are about 2.5-3.0 gram-atomsand about 0.8-1.0 mole respectively. In batch operations, the reactantsare introduced at levels to provide these ranges. In semi-continuous andcontinuous operations, they may be admixed at any ratio but on a massbalance basis, they are present so as to be consumed in amounts withinthese ratios.

[0035] The temperature range in which the sulfurization reaction iscarried out is generally about 50° C.-350° C. The preferred range isabout 170° C.-300° C., with about 175° C.-225° C. being especiallysuitable. At the “low” temperatures, generally below about 140° C.sulfurization reaction generally favors formation of polysulfides andnot the preferred dithiones. The reaction can be conducted underatmospheric pressure or at elevated pressures. Elevated pressures can beby autogenous pressure (i.e., the pressure which naturally developsduring the course of the reaction) but may also be externally appliedpressure. The exact pressure developed during the reaction is dependentupon such factors as the design and operation of the system, thereaction temperature, and the vapor pressure of the reactants andproducts and it may vary during the course of the reaction. Preferredprocess pressures are at atmospheric to about 500 psig. In a preferredaspect, hydrogen sulfide liberated in the reaction is neutralized orremoved, such as via a scrubber or other suitable means. The presence ofhydrogen sulfide can reduce the yield of the desiredpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compositions byforming side reactions with the HR PIB, sulfur and mercaptan products.In such instance excess HR PIB can be employed.

[0036] It is frequently advantageous to incorporate materials useful assulfurization catalysts in the reaction mixture. Typically these areacidic (such as sulfonic acid, boric acid) or basic materials (such asinorganic oxides and salts such as sodium hydroxide, calcium oxide andsodium sulfide); with the most desirable being nitrogen bases includingammonia and amines. The amines include primary, secondary and tertiaryhydrocarbyl amines wherein the hydrocarbyl radicals are alkyl, aryl,aralkyl, alkaryl or the like and contain about 1-20 carbon atoms.Suitable amines include aniline, benzylamine, dibenzylamine,dodecylamine, naphthylamine, tallow amines, N-ethyldipropylamine,N-phenylbenzylamine, N,N-diethylbutylamine, m-toluidine and2,3-xylidine. Also useful are heterocyclic amines such as pyrrolidine,N,N-methylpyrrolidine, piperidine, pyridine and quinoline. The preferredbasic catalysts include ammonia and primary, secondary, or tertiaryalkylamines having about 1-8 carbon atoms in the alkyl radicals.Representative amines of this type are methylamine, dimethylamine,trimethylamine, ethylamine, diethylamine, triethylamine,di-n-butylamine, tri-n-butylamine, tri-sec-hexylamine andtri-n-octylamine. Mixtures of these amines can be used, as well asmixtures of ammonia and amines. It is also believed that addition of thedesired polyisobutyl-1,2-dithiole-4-cyclopentene-3-thione product to thereaction mixture may act as a catalyst.

[0037] The amount of catalytic material used is generally about0.05-2.0% of the weight of the HR PIB compound. In the case of thepreferred ammonia and amine catalysts, about 0.0005-0.5 mole per mole ofolefin is preferred, and about 0.001-0.1 mole is especially desirable.

[0038] Also present in the reaction mixture may be water, either as acatalyst or as a diluent for one or more of the catalysts recitedhereinabove. The amount of water, when present, is usually about 1-25%by weight of the HR PIB compound. The presence of water is, however, notessential and when certain types of reaction equipment are used it maybe advantageous to conduct the reaction under substantially anhydrousconditions.

[0039] The method of this invention is usually carried out in theabsence of solvents and diluents other than water. However, it maysometimes be desirable to use a substantially inert, nomially liquidorganic diluent in the reaction. The nature of suitable diluents willreadily be apparent to those skilled in the art.

[0040] The time required for the reaction to be completed will varydepending on the reagents, ratios thereof, the reaction temperature, thepresence or absence of catalysts, and the purity of the reagents. Thecourse of the reaction is conveniently followed by monitoring thepressure in the reaction vessel; the reaction can be considered completewhen the pressure levels off to a constant value.

[0041] Following the preparation of the sulfurized mixture by theprocedure described hereinabove, substantially all low boiling materialsare removed. The nature of these low boiling materials will varyaccording to the amount and type of reactants used and the reactionconditions. It will also vary to some extent according to the use towhich the sulfurized product is to be put, as well as such things asodor and flammability considerations, recycling needs of reactants andby-products, and the like. Most often, the product should have a flashpoint above about 30° C., preferably above 70° C. and desirably aboveabout 100° C. as determined by ASTM Procedure D93. Reference is alsomade to ASTM Procedures D56 and D13 10.

[0042] In addition to starting materials such as the HR PIB compound(s),the low boiling materials will often include unreacted startingmaterials and solids which can be removed. In addition, mercaptans andmonosulfides, especially when the starting olefin contains less than 9carbon atoms, and under those circumstances it is preferred that theproduct contain no more than about 5% by weight of such startingmaterials, mercaptan and monosulfides. If these materials are gaseous atambient pressure and temperature, they may be removed in part simply byventing the reaction vessel, and they may be recycled if desired. In thecase of less volatile starting materials, it may be necessary to resortto such techniques as distillation at atmospheric pressure or vacuumdistillation or stripping. Another useful method is the passage of aninert gas such as nitrogen through the mixture at a suitable temperatureand pressure. Large scale gas chromatography and molecular distillationmay also be useful.

[0043] Any solids present in the reaction mixture may be convenientlyremoved, in most instances, by decanting the liquid product. If furtherremoval of solids is desired, such conventional techniques as filtrationor centrifugation may be used.

[0044] A further optional step in the method of this invention is thetreatment of the sulfurized product, obtained as described hereinabove,to reduce active sulfur. By “active sulfur” is meant sulfur in a formwhich can cause staining of copper and similar materials. Standard testsare available to determine sulfur activity. As an alternative to thetreatment to reduce active sulfur, metal deactivators can be used in thelubricants containing the sulfurized compositions of this invention. Insome instances, such as in metal working lubricants, high levels ofactive sulfur may be desired and it may then be preferred not to reduceactive sulfur.

[0045] When active sulfur is to be reduced, any of several methods knownin the art may be employed. An illustrative method is treatment with analkali-metal sulfide as described in U.S. Pat. No. 3,498,915.

[0046] Specific fractions of thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thiones can further separatedinto more pure components through various techniques. For example,distillation of the mixture can lead to various purities of thefractions. Also, if lower boiling point components such as the C₈H₁₆isomers are desired to be removed the reaction can be carried out underatmospheric conditions using reflux to have a C₈ fraction and a C₁₂₋₃₂fraction. These fractions can be further purified into predominatelyC₁₂, C₁₆, C₂₀, C₂₄, C₂₈, or C₃₂ fractions or mixtures thereof, includingmixtures with C₈ prior to the sulfurization reaction or subsequentthereto. Preferably the variouspolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione isomers are enrichedto be at least 10 wt. % and more preferably at least 30 wt. % and mostpreferably at least 50 wt. % of the total composition. Under certaincircumstances substantially purified isomers can be obtained.

[0047] Other optional treatments may be employed to improve suchqualities as the odor, color and staining characteristics of thesulfurized compositions. These may include treatment with acidic clayssuch as Super Filtrol and filtration through fuller's earth, activatedcharcoal, alumina clays or the like. Such treatments are often notrequired when a basic catalyst is employed.

[0048] If desired, the polyisobutyl-1,2-dithiole-4-cyclopentene-3-thionecompositions can oxidized with a peroxidic compound to for the resultingpolyisobutenyl-1,2-dithiole-3-one composition(s). The thiocarbonyl groupcan be readily converted to a carbonyl group by treatment with aqueouspotassium permanganate, or aqueous mercuric acetate, or by chlorinationfollowed by hydrolysis.

[0049] Lubricating Compositions

[0050] The lubricating oil compositions of the present invention can beconveniently prepared by simply blending or mixing the compositionprepared by sulfurization of a highly reactive polyisobutylene having atleast 25% of a methylvinylidene isomer and wherein the polyisobutylenehas a number average molecular weight in the range of about 120 to about600 with a sulfur source at a reaction temperature in excess of about175° C. with an oil of lubricating viscosity (base oil). The oil oflubricating viscosity may be mixed with the resultingpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compositions of thepresent invention, typified by Formula I. The compounds of the inventionmay also be preblended as a concentrate or package with various otheradditives in the appropriate ratios to facilitate blending of alubricating composition containing the desired concentration ofadditives. The compounds of the present invention are blended with baseoil a concentration at which they provide wear protection and are bothsoluble in the oil and compatible with other additives in the desiredfinished lubricating oil. Compatibility in this instance generally meansthat the present compounds as well as being oil soluble in theapplicable treat rate also do not cause other additives to precipitateunder normal conditions. Suitable oil solubility/compatibility rangesfor a given compound of lubricating oil formulation can be determined bythose having ordinary skill in the art using routine solubility testingprocedures. For example, precipitation from a formulated lubricating oilcomposition at ambient conditions (about 20° C.-25° C.) can be measuredby either actual precipitation from the oil composition or theformulation of a “cloudy” solution which evidences formation ofinsoluble wax particles.

[0051] If an engine oil formulation is desired, typically thelubricating oil composition of the invention contains about from 0.01 to5 wt. %, preferably 0.05 to 3 wt. %, more preferably about from 0.05 to1 wt. % based on the total weight of the composition, of a wearprotectant selected from the lubricating oil soluble sulfurizedcompounds prepared by reacting a polyisobutylene having a number averagemolecular weight in the range of about 120 to about 600 with a sulfursource at a reaction temperature in excess of 175° C. Especiallypreferred are components of formula 1, derivatives, and mixturesthereof. More preferably, the lubricating composition contains aboutfrom 0.1 to 1 wt. % of said wear protectant. The present compounds arecompatible with, and can be advantageously used with, zincdithiophosphates to increase wear protection or more preferably toreduce the amount of zinc dithiosphosphate which would otherwise berequested to provide a given level of wear protection. If a gear oilformulation is desired, typically the lubricating oil composition of theinvention contains about from 0.01 to 10 wt. %, preferably 0.5 to 8 wt.%, more preferably about from 1 to 5 wt. %, and even more preferablyfrom about from 2 to 4 wt. %, of the sulfurized reaction product of thisinvention and even more preferably the compounds of formula I, based onthe total weight of the composition.

[0052] The lubricating oil, or base oil, used in the lubricating oilcompositions of the present invention are generally tailored to thespecific use e.g. engine oil, gear oil, industrial oil, cutting oil,etc. For example, where desired as an engine oil, the base oil typicallywill be a mineral oil or synthetic oil of viscosity suitable for use inthe crankcase of an internal combustion engine such as gasoline enginesand diesel engines which include marine engines. Crankcase lubricatingoils ordinarily have a viscosity of about 1300 cSt at 0° F. to 24 cSt at210° F. (99° C.) the lubricating oils may be derived from synthetic ornatural sources. Mineral oil for use as the base oil in this inventionincludes paraffinic, naphthenic and other oils that are ordinarily usedin lubricating oil compositions. Synthetic oils include both hydrocarbonsynthetic oils and synthetic esters. Useful synthetic hydrocarbon oilsinclude liquid polymers of alpha olefins having the proper viscosity.Especially useful are the hydrogenerated liquid oligomers of C₆ to C₁₂alpha olefins such as 1-decene trimer. Likewise, alkyl benzenes ofproper viscosity such as didodecyl benzene can be used. Useful syntheticesters include the esters of both monocarboxylic acid and polycarboxylicacids as well as monohydroxy alkanols and polyols. Typical examples aredidodecyl adipate, pentaerythritol tetracaproate, di-2-ethylhexyladipate, dilaurylsebacate and the like. Complex esters prepared frommixtures of mono and dicarboxylic acid and mono and dihydroxy alkanolscan also be used. Blends of various mineral oils, synthetic oils andminerals and synthetic oils may also be advantageous, for example toprovide a given viscosity or viscosity range. In general the base oilsor base oil mixtures for engine oil are preselected so that the finallubricating oil, containing the various additives, including the presentwear protectant, has a viscosity at 100° C. of 4 to 22 centistokes,preferably 10 to 17 centistokes and more preferably 13 to 17centistokes.

[0053] Typically the lubricating oil composition will contain a varietyof compatible additives desired to impart various properties to thefinished lubricating oil composition depending on the particular end useand base oils used. Such additives include neutral and basic detergentssuch as natural and overbased organic sulfonates and normal andoverbased phenates and salicylates, dispersants, ashless dispersantssuch as various polyalkylsuccinimides or polyalkylsuccimic acid esters,rust inhibitors, foam inhibitors, pour point dispersants, antioxidants,including the so called viscosity index (VI) improvers, dispersant VIimprovers and, as noted above, other corrosion or wear inhibitorsincluding oxidation inhibitors such as phenol compounds and aminecompounds; defoaming agents such as dimethylpolysiloxane andpolyacrylate; friction modifiers such as higher fatty acids, higheralcohols, aliphatic amines, fatty acid amides, esters of fatty acids,sulfurized fats, acidic phosphate esters, acidic phosphite esters,organic molybdenum compounds, and solid lubricants; corrosion inhibitorssuch as benzotriazole and thiazole; viscosity index improvers (which maybe active type having increased dispersability) such as acrylic polymer,methacrylic polymer and olefin copolymer; and pour point depressantssuch as acrylic polymer, methacrylic polymer, polybutene,polyalkylstyrene and polyvinylacetate. Some of these additives arefurther described below.

[0054] Suitable oil soluble phosphorous containing agents include estersprepared from phosphorous acid and aliphatic or aromatic alcohols(dilauryl phosphate, diphenyl phosphate, dioleyl phosphate, mono &dibutyl phosphate) and esters prepared from phosphoric acid andaliphatic or aromatic alcohols (monooctyl phosphate, dioctyl phosphate,trioctyl phosphate, etc.). Dimethyl esters of aliphatic phosphonic acidsin which the aliphatic group has an average in the range of about 12 toabout 24 carbon atoms are fully described in U.S. Pat. No. 4,158,633.The aliphatic group can be saturated or unsaturated, and branched orstraight chain in structure. Preferred are the dimethyl esters ofaliphatic phosphonic acids wherein the aliphatic group has an average inthe range of about 16 to about 20 carbon atoms. Most preferred are thephosphonate esters wherein the aliphatic group is relatively pure andcontains about 18 carbon atoms or a mixture of phosphonate esters inwhich the aliphatic groups contain an average of about 18 carbon atoms,such as mixture derived from commercial technical grades of oleylchloride.

[0055] Typical metal-free phosphorus-containing antiwear and/or extremepressure additives used in the practice of this invention include estersof phosphorus acids, amine salts of phosphorus acids and phosphorusacid-esters. Examples of suitable compounds which may be used asphosphorus-containing antiwear and/or extreme pressure agents includetrihydrocarbyl phosphites, phosphonates and phosphates, anddihydrocarbyl phosphites; such as tricresyl phosphate, cresyl diphenylphosphate, tributyl phosphate, trioleyl phosphate, trilauryl phosphate,tributyl phosphite, trioctyl phosphite, triphenyl phosphite, tricresylphosphite, tricyclohexyl phosphite, dibutyl lauryl phosphonate, dibutylhydrogen phosphite, dioleyl hydrogen phosphite, and tolyl phosphinicacid dipropyl ester. Among the amine salts which can be employed areamine salts of partially esterified phosphoric, phosphorous, phosphonic,and phosphinic acids; amine salts of phosphonic acids and the like.Specific examples include the dihexylammonium salt of dodecylphosphoricacid, the diethyl hexyl ammonium salt of dioctyl dithiophosphoric acid,the octadecylammonium salt of dibutyl phosphoric acid, thedilaurylammonium salt of 2-ethylhexylphosphoric acid, the dioleylammonium salt of butane phosphonic acid, and analogous compounds.

[0056] The ester, amide or amine salt portion of the dithiophosphatewill generally have from 1 to 20 carbons, preferably 4 to 10 carbons,and from 0 to 5 nitrogens (when the amide or amine salt is employed,that portion preferably has from 1 to 3 nitrogens with the carbon tonitrogen atomic ratio preferably ranging from 1 to 10). The ester, amideor amide salt portion of the dihydrocarbyl dithiophosphate antiwearagent will contain stable organic moieties such as hydrocarbon orethoxylated hydrocarbon groups.

[0057] Exemplary dihydrocarbyl dithiophosphate amides include the ethylamide of di-4-methyl-2-pentyl dithiophosphate, the butyl amide ofdiisoctyl dithiophosphate, the aminoethyl amide of ditetrapropenylphenyldithiophosphate, the diamino diethylene amide of ditetrapropenylphenyldithiophosphate, and diamino diethylene amide of di-2-ethyl-1-hexyldithiophosphate.

[0058] Metal containing phosphorus compounds are formed by reacting adihydrocarbyl dithiophosphoric acid with a metal oxide, for example zincoxide, The hydrocarbyl portion of the dithiophosphoric acid will usuallyhave from 4 to 20 carbons, preferably from 5 to 12 carbons, and morepreferably from 6 to 8 carbons. As referred to herein, the term“hydrocarbyl” represents a monovalent organic radical composedessentially of hydrogen and carbon, but minor amounts of inertsubstituents may be present. The hydrocarbyl may be aliphatic, aromaticor alicyclic or combinations thereof, for example, aralkyl, alkyl, aryl,cycloalkyl, alkylcycloalkyl, etc., and may be saturated or olefinicallyunsaturated. Exemplary hydrocarbyl groups include methyl, ethyl, propyl,butyl, pentyl, 4-methylpentyl, 2-ethylhexyl, hexyl, octyl, isooctyl,stearyl, phenyl, benzyl, ethylbenzyl, amyl, propenylphenyl,dipropenylphenyl, tetrapropenylphenyl, tolyl, etc. The primary,secondary or tertiary hydrocarbyl groups may be employed, but thebranched-chain, primary groups are preferred, even more preferred aremixtures of aliphatic groups and in a preferred embodiment, at least 75mole percent of sec-butyl alcohol is used and preferably combined with4-methyl-2-pentanol, and most preferably further combined with a zincmetal. Particularly preferred metal dihydrocarbyl phosphorodithioatesinclude the zinc dithiophosphates. Patents describing the synthesis ofsuch zinc dithio-phosphates include U.S. Pat. Nos. 2,680,123; 3,000,822;3,151,075; 3,385,791; 4,377,527; 4,495,075 and 4,778,906. Each of thesepatents is incorporated herein by reference in their entirety.

[0059] Exemplary zinc dihydrocarbyl dithiophosphates include zincdi-n-octyl dithiophosphate, zinc butyl isooctyl dithiophosphate, zincdi-4-methyl-2-pentyl dithiophosphate, zinc ditetrapropenylphenyldithiophosphate, zinc di-2-ethyl-1-hexyl dithiophosphate, zinc diisoctyldithiophosphate, zinc dihexyl dithiophosphate, zinc diphenyldithiophosphate, zinc diethylphenyl dithiophosphate, zinc diamyldithiophosphate, zinc butyl phenyl dithiophosphate, zinc dioctadecyldithiophosphate.

[0060] Alkali-metal borates or hydrates thereof are well known in theart as extreme pressure additives and are available commercially.Examples of the alkali-metal borates or hydrates thereof includepotassium borate hydrate and sodium borate hydrate represented byKB₃O₅.H₂O and NaB₃O₅.H₂O, respectively. These alkali-metal boratehydrates are, for example, prepared by the steps of dissolving potassium(or sodium) hydroxide and boric acid in water so that the atomic ratioof boron to alkali-metal (potassium or sodium) would be in the range of2.0 to 4.5 (boron/alkali-metal), dispersing the solution in an oilysolution containing a neutral alkaline earth metal sulfonate or anashless dispersant of succinic imide type, and allowing it to react toobtain the desired hydrate in the form of a dispersion liquid of fineparticles. The gear lubricating oil composition of the inventioncomprises the alkali-metal borate or hydrate thereof in an amount of0.04 to 1.0 wt. % in terms of boron content, preferably 0.05 to 0.6 wt.%, more preferably 0.08 to 0.5 wt%. This amount corresponds to about 0.6to 15 wt. % of alkali-metal borate or hydrate thereof in the lubricatingoil composition, if OLOA9750 (dispersion liquid of potassium boratehydrate, commercially available from Chevron Oronite Company LLC,Houston Tex., boron content: 6.8 wt. %)is employed as the alkali-metalborate.

[0061] One type of copper corrosion inhibitors which can be used in thepractice of this invention is comprised of thiazoles, triazoles andthiadiazoles. Examples include benzotriazole, tolyltriazole,octyltriazole, decyltriazole, dodecyltriazole, 2-mercap-tobenzothiazole,2,5-dimercapto-1,3,4-thiadiazole,2-mercapto-5-hydrocarbylthio-1,3,4-thiadiazoles,2-mercapto-5-hydrocarbyldithio-1,3,4-thiadiazoles,2,5-bis(hydrocarbylthio)-1,3,4-thiadiazoles, and2,5-bis(hydrocarbyldithio)-1,3,4-thiadiazoles. The preferred compoundsare the 1,3,4-thiadiazoles, especially the2-hydrocarbyldithio-5-mercapto-1,3,4-dithiadiazoles and the2,5-bis(hydrocarbyldithio)-1,3,4-thiadiazoles, a number of which arecommercially available. Other suitable inhibitors of copper corrosioninclude ether amines; polyethoxylated compounds such as ethoxylatedamines, ethoxylated phenols, and ethoxylated alcohols, imidazolines; andthe like.

[0062] Suitable antifoam agents for use in the compositions of thisinvention include silicones and organic polymers such as acrylatepolymers. Mixtures of silicone-type antifoam agents such as the liquiddialkyl silicone polymers with various other substances are alsoeffective. Typical of such mixtures are silicones mixed with an acrylatepolymer, silicones mixed with one or more amines, and silicones mixedwith one or more amine carboxylates. Other such mixtures includecombinations of a dimethyl silicone oil with (i) a partial fatty acidester of a polyhydric alcohol (U.S. Pat. No. 3,235,498); (ii) analkoxylated partial fatty acid ester of a polyhydric alcohol (U.S. Pat.No. 3,235,499); (iii) a polyalkoxylated aliphatic amine (U.S. Pat. No.3,235,501); and (iv) an alkoxylated aliphatic acid (U.S. Pat. No.3,235,502).

[0063] The formulations may also contain a rust inhibitor. This may be asingle compound or a mixture of compounds having the property ofinhibiting corrosion of ferrous metal surfaces. Such materials includeoil-soluble monocarboxylic acids such as 2-ethylhexanoic acid, lauricacid, myristic acid, palmitic acid, oleic acid, linoleic acid, linolenicacid, behenic acid, cerotic acid, etc., and oil-soluble polycarboxylicacids including dimer and trimer acids, such as are produced from talloil fatty acids, oleic acid, linoleic acid, or the like. Other suitablecorrosion inhibitors include alkenylsuccinic acids in which the alkenylgroup contains 10 or more carbon atoms such as, for example,tetrapropenylsuccinic acid, tetradecenylsuccinic acid,hexadecenylsuccinic acid, and the like; long-chainalpha-omega-dicarboxylic acids in the molecular weight range of 600 to3000; and other similar materials.

[0064] When lubricating compositions contain on or more of the abovementioned additives, each additive is typically blended into the baseoil in an amount which enables the additive to provide its desiredfunction. Representative effective amounts listed as mass percent activeingredients when used as an engine oil and preferably a crankcaselubricant are illustrated herein: ashless dispersant from 0.1 to 20 andpreferably 1-8; detergent from 0.1 to 15 and preferably 0.2 to 9; metaldialkyl dithiophosphate from 0.01 to 6 and preferably 0.05 to 5 basedupon phosphorous content; antioxidant from 0 to 5 and preferably 0.01 to1.5; pour point depressant from 0.01 to 5 and preferably 0.01 to 1.5;antifoaming agent from 0 to 5 and preferably 0.001 to 0.15; supplementalantiwear agents from 0 to 0.5 preferably 0 to 0.2; friction modifierform 0 to 3 and preferably 0 to 1; viscosity modifier from 0 to 6 andpreferably 0.01 to 4. Additionally, these additives may be added to agear oil formulation in the ranges depicted above. However, preferably agear lubricating composition comprises: a major amount of oil oflubricating viscosity; 0.01 to 10 wt. % preferably 0.5 to 8.0 wt. % interms of sulfur content of a sulfurized olefin prepared by reacting apolyisobutylene having at least 25% of a methylvinylidene isomer andwherein the polyisobutylene has a number average molecular weight in therange of about 120 to about 600 with a sulfur source at a reactiontemperature in excess of 175° C.; 0.05 to 5.0 wt. % in terms ofphosphorous content of at least one oil soluble phosphorous containingcompound selected from extreme pressure agents and antiwear agents; 0.04to 1.0 wt. % in terms of boron content of an alkali-metal borate orhydrate thereof Additionally such gear lubricating further comprises atleast one of the following additional components: 0.1 to 5 wt. % basedupon the weight of said lubrication composition of at least one ashlessdispersant; 0.1 to 0.8 wt. % based upon the weight of said lubricationcomposition of at least one copper corrosion inhibitor; 0.01 to 0.1 wt.% based upon the weight of said lubrication composition of at least onefoam inhibitor; and, 0.01 to 0.1 wt. % % based upon the weight of saidlubrication composition of at least one antirust agent.

[0065] The present lubricating compositions also include greasescontaining the present oil such as the base oils described above as wellas more viscous mineral, natural, or synthetic oils and a thickeningagent to provide the desired consistency to the grease. The base oil isgenerally used in an amount sufficient to balance the total greasecomposition, after accounting for the desired quantity of the thickeningagent, and other additive components including in the greaseformulation. A wide variety of materials can be employed as thickeningor gelling agents. These can include fatty acid metal salts or soaps,such as calcium, or lithium stearates or hydroxystearates, which aredispersed in the lubricating vehicle in grease-forming quantities in anamount sufficient to impart to the resulting grease composition thedesired consistency. Other thickening agents that can be employed in thegrease formulation comprise the non-soap thickeners, such assurface-modified clays and silicas, aryl ureas, calcium complexes andsimilar materials. In general, grease thickeners can be employed whichdo not melt or dissolve when used at the required temperature within aparticular environment; however, in all other respects, any materialwhich is normally employed for thickening or gelling hydrocarbon fluidsfor forming greases can be used in the present invention.

[0066] The present invention also provides an additive package orconcentrate which may be added to an oil of lubricating viscosity eitheras the sole additive or in combination with other additives. (Generally,the additive package will not contain a viscosity index improver becauseeven where desired the viscosity index improver is generally added tothe base oil by the lubricant formulator.) Thus, a preferred additiveconcentrate contains about from 0.5 to 50 wt. % more preferably 1 to 40wt. % of the sulfurized polyisobutylene reaction product and compound offormula I of the present invention and sufficient basic material(typically overbased detergents) to provide the concentrate with a TBNof about from 60 to 180 preferably 60 to 120; and about 1 to 10 wt. %preferably 2 to 6 wt. % of a diluent oil or other compatible inertorganic liquid diluent. With the general exception of the VI improver,the concentrate will frequently also contain various other additivesconsidered desirable from the intended use and generally will containabout from 30 to 60 wt. % of an ashless dispersant and frequently willalso contain neutral or slightly alkaline detergent in addition to theoverbased detergent. The amount of overbased detergent needed to providethe requisite TBN will, of course, vary with the TBN of the overbaseddetergent but typically will be 20 to 80 wt. % of the concentrate. Theconcentrate may also be provided as an individual concentrate containingabout from 85 to 95 wt. % of the present sulfurized reaction product orcompound of formula I and about 5 to 15 wt. % of an inert organic liquiddiluent designed for formulation either into an additives package ordirectly into the base oil. Additive packages or concentrates may alsobe provided for greases, though generally such packages will containlittle more than the compounds of the present invention and perhapsother antiwear or extreme pressure agents.

[0067] Included in the lubricating oil compositions of the presentinvention are engine oils such as diesel engine oils, as noted above,including those used in marine diesel engines, locomotives, power plantsand high speed automotive diesel engines, gasoline burning engines andcompressors; functional fluids including automotive fluids such asautomatic transmission fluids, power steering fluids and power brakefluids; gear oils including such oils are automotive spiral-bevel andworm-gear axle oils which operate under extreme pressures, load andtemperature conditions, hypoid gear oils operating under both highspeed, low torque and low speed, high torque conditions and variousother industrial oils and cutting oils.

[0068] The various additive materials or classes of materials describedabove are known materials and can be prepared by known procedures orobvious modifications thereof and frequently are readily available fromcommercial sources. A listing of various additives and their function isfor example described in columns 9 and 10 of U.S. Pat. Nos. 4,119,549and 5,397,486, hereby incorporated by reference.

EXAMPLES

[0069] The following examples are included to demonstrate preferredembodiments of the invention. It should be appreciated by those of skillin the art that the techniques disclosed in the examples that follow mayrepresent techniques discovered by the inventor to function well in thepractice of the invention, and thus may be considered to constitutepreferred modes for its practice. However, those of skill in the artshould, in light of the present disclosure, appreciate that many changesmay be made in the specific embodiments that are disclosed and stillobtain a like or similar result without departing from the spirit andscope of the invention.

Comparative Example A Preparation of sulfurized isobutylene

[0070] Saturated dialkyl polysulfides from reacting isobutylene withhydrogen sulfide and elemental sulfur can be represented by thefollowing reaction scheme:

[0071] Typically these compounds are prepared via a two step processwhere t-butyl mercaptan is generated in the first step, followed bysulfurization to yield di-t-butyl polysulfides. By carefully controllingreaction conditions mixtures and predominately separated fractions ofdi-sulfides, tri-sulfides and tetra-sulfide di-t-butyl polysulfidecompounds can be formed. These reaction products were characterized byGCMS; four major products were detected. These products are evidenced inthe gas chromatogram by four major peaks with increasing retention timescorresponding to the di-, tri-, tetra-, and penta- sulfidesrespectively. The compounds were characterized by the mass spectra; foreach compound, a molecular ion is present (i.e. 178, 210, 242, and 274m/z for the sulfides listed), and a base peak at 57 m/z attributed tothe t-butyl fragment ion. These compounds are commercially available,for example C₈H₁₈S_(x) here x averages 3 and 4 are available as TBPS 344and TBPS 454, respectively, from Chevron Phillips Chemical Company LP,Houston Tex. The latter was used herein as Comparative Example A.

Comparative Example B Preparation of sulfurized isobutylene complexmixtures

[0072] More complex alkyl-alkenyl type polysulfide mixtures can beformed by changing reaction conditions, temperature reactant charging orby employing a catalyst. The alkyl-alkenyl products formed are presentedby the following scheme:

[0073] These reaction products contain a mixture of alkyl-alkenyl typepolysulfide products with alkyl/alkenyl disulfide and alkyl/alkenyltrisulfide as predominate components. The mixtures also contain cyclictrisulfide, dialkenyl sulfides and disulfides, alkyl/dialkenyl di- andtrisulfides as well as other sulfides. These products were alsocharacterized by GCMS. The following table outlines the structures,identified from the mass spectra, for the majority of the compoundsdetected in a typical sample; includes are the mass/charge ratios of themolecular ions observed, and the concentrations for a typical sample.TABLE 1 Sulfurized isobutylene complex mixtures Molecular Ion, WeightSulfide Structure m/z %

140 2-5

176 15-20

208 25-30

230 1-5

262  3-10

[0074] Commercially available products are sold as Vanlube SB,Vanderbilt Company Inc., Norwalk Conn. and Mobilad C-100, ExxonMobilChemical Company of which the latter was used herein as ComparativeExample B.

Comparative Example C Sulfurization of commercially availabletriisobutylene

[0075] A typical commercially available triisobutylene (TCI America)having less than 2% methylvinylidene, contained about 45%2,2,6,6-tetramethyl-4-methylene heptane and about 53%2,2,4,6,6-pentamethyl-3-heptene was treated 2.5 mole equivalents ofsulfur. 362.9g (2.16mol) of the triisobutylene and 173g (5.4mol) ofsulfur were reacted under conditions similar to those described inexample 2. After about 6 hours at about 180° C. (reflux), the yield ofsulfurized products was 4% which included less than 1% of4,5-dialkyl-1,2-dithiole-4-cyclopentene-3-thione by GCMS. The alkylgroups on the dithiolethione were t-butyl and neopentyl as evidenced inthe mass spectrum which included the molecular ion, 260 m/z, andfragment ions 57, 189, 203, 227, and 245 m/z.

Preparation of Sulfurized Polyisobutylene Oligomers of the invention:Example 1 Preparation ofpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione “PDCT” mixtures from ahigh methyl vinylidine C₈-C₃₂ polyisobutene fraction.

[0076] 1904.8g (I0.7mol) of a high methyl vinylidine content lowmolecular weight PIB having a number average molecular weight of 178,approximately 74% methyl vinylidine content (and a weight fraction ofeach oligomer of approximately 16 wt. % C₈H₁₆, about 41 wt. % C₁₂H₂₄,about 26 wt. % C₁₆H₃₂, about 11 wt. % C₂₀H₄₀, about 4 wt. % C₂₄H₄₈, andabout 2 wt. % C₂₈H₅₆ with trace amounts of C₃₂H₆₄ as characterized bygas chromatography and nuclear magnetic resonance spectroscopy) and1017.5g of elemental sulfur were charged to a 5 liter stainless steelautoclave. The autoclave was flushed with nitrogen, and then sealed. Thereactants were stirred and heated to 200° C. over about 2 hours. Thetemperature was then maintained between 200 and 220° C. under autogenouspressure for 3.5 hours such that the pressure in the autoclave did notexceed 200 psia. The reaction was cooled to ambient temperature and theautoclave was vented through a caustic scrubber. 2440 g of a dark redoil was diluted with pentane, filtered, and then stripped to removesolvent. Product contained 29.3% sulfur, as analyzed with a LECO SC-32sulfur analyzer by ASTM D1552, and 49.5% of the PDCT's of formula I ascharacterized by GCMS.

Example 2 Preparation of PDCT mixtures from a high methyl vinylidineC₁₂-C₃₂ polyisobutene fraction:

[0077] 497.4g (2.5 1mol) of a low molecular weight polybutene that hadbeen distilled to remove the C₈ isomers, having a number averagemolecular weight of 198 and 73% methyl vinylidene content, and 201g ofsulfur were heated and stirred, under a nitrogen atmosphere, in a 3 neckglass round bottom flask equipped with a mechanical stirrer, heatmantle, thermocouple, temperature controller, reflux condenser, nitrogeninlet, and caustic scrubber. A gentle sweep of nitrogen was continuouslypassed through the vessel and scrubber. The reactants were heated toreflux, at about 180° C., then slowly heated to 200° C. over a total ofabout 1 hour; they were held at 200° C. for about 20 minutes, thenheated at 220° C. for 2.5 hours. After cooling to room temperature theproduct was diluted with 400 ml of heptane and filtered throughdiatomaceous earth. The solvent was removed to yield 447.4 g of a darkred, viscous oil that contained 23.8% sulfuir.

Example 3 Preparation of PDCT from Isobutene Tetramer

[0078] A distillation fraction containing C₁₆ isomers, that includedabout 66 wt% methylvinylidene, from polyisobutene was sulfurized in amanner similar to example 2. The products of this Example werecharacterized by gas chromatography mass spectroscopy (GCMS) analysis.The following table contains molecular structures or empirical formulas,mass charge ratios for molecular ions observed, and weight percent ofthe majority of the composition. TABLE 2 Sulfurized reaction productfrom high methyl-vinylidene isobutene tetramer Sulfide Molecular Ion,m/z Weight % C₁₆H₂₈S 252 1.2 C₁₆H₃₂S₂ 288 1.5 C₁₆H₂₈S₂ 284 3.2

316 38.3 (C₁₆H₃₃)₂S₂ 514 15.4 (C₁₆H₃₃)₂S₃ 546 3.1

[0079] The polyisobutyl-1,2-dithiole-4-cyclopentene-3-thiones, wherein nis zero R₁ is methyl and n is one R₁ is hydrogen; are the major productsand account for about 40% of the product by weight; the mass spectrum ofthis compound exhibits a molecular ion at 316 m/z with a ³⁴S isotopepeak (m+2 peak) corresponding to three sulfur atoms per molecule andfragment ions at 41, 57, 148, 189 and 203 m/z. Characteristic of thePDCT's is an intense 148 m/z fragment ion peak. Thedi-tetraisobutyl-polysulfides are the second most abundant compound typepresent in the mixture; the mass spectrum for the disulfide exhibitedthe molecular ion at 514 m/z with the ³⁴S isotope peak corresponding twosulfur atoms per molecule, and fragment ions at 41, 57, 69, 97, 113, and129 m/z. It is anticipated that the yield of PDCT's could be increased.The compounds of this invention may be purified, for example bydistillation or chromatography.

Example 4 Purification ofpolyisobutyl-1,2-dithiole-4-cyclopentene-3-thiones (PDCT's of Example1):

[0080] A sample from Example 1 was purified by HPLC on a silica gelcolumn. The column was flushed with hexane to remove unreacted HR PIBand sulfuir containing compounds other than PDCT's. Fractions containingthe desired dithiolethiones were collected using hexane:ethyl acetate9:1 as eluent. Removal of solvent from a set of fractions yielded aproduct that contained 88.4 weight percent of C_(8,12,16,20) PDCT's byGC; the product contained about 33% sulfur.

Performance Examples

[0081] The following examples tested the antiwear properties, extremepressure properties and oxidation properties. The base line formulationemployed a formulated oil. This formulated oil comprised a lubricatingoil and additives in their typical amounts for particular purpose; thisincluded a Group TI base oil of a viscosity grade of 5W20, 3 wt. % of a2300 molecular weight post treated ethylene carbonate bissuccinimidedispersant, 1 wt. % of a low overbase TBN 17 calcium sulfonate, 2.4 wt.% of a high overbase TBN 250 calcium phenate, 0.6 wt% of a secondaryalcohol ZnDTP, 0.5 wt. % of a diphenyl amine antioxidant, and aviscosity index improver. This formulation is referred to herein as alow phosphorous basestock since the phosphorous content is approximately0.08 wt. % on the basis of total phosphorous in the lubricatingcomposition.

Example 5 Anti-wear properties Four Ball Wear Test

[0082] The Four Ball Wear Test was preformed in a manner similar to ASTMD-4172 (4-ball wear), as described below. Samples of thepolyisobutyl-1,2-dithiole-4-cyclopentene-3-thione compounds preparedaccording to Example 1, Example 3, and a commercially availablesulfurized isobutylene (Comparative Example A), were top-treated to thebaseline low phosphorus automotive crankcase engine oil at a treat rateof 0.2 to 0.25 weight percent to the above formulation according to thefollowing table. These formulated test oils were aged in an oxidationbath, containing steel ball bearings, for 48 hours at 160° C. with15L/hour of airflow bubbled through the oil. These aged oils were testedon a 4-ball wear test apparatus using 100 C6 steel balls; 90kg load wasapplied in 9 stages starting from 10 kg with 10 kg increments at 1500rotations per minute. The wear index was calculated from movement of theload arm.

[0083] Table 3 shows the wear test results. The products of Example 1and Example 3 were both more effective at controlling wear than thebaseline formulation alone or the baseline with Comparative Example Awhich in contrast, gave performance worse than the baseline. The productof Example 1 gave significantly better performance compared to thebaseline. TABLE 3 Wear index results SAMPLE Treat rate, % S basis WearIndex Basestock (base line) 0 179 Example 1¹ 0.059 82 Example 3¹ 0.039165 Comparative A¹ 0.054 331

Example 6 Extreme pressure properties: Falex Extreme pressure wear test

[0084] The products of Example 2, Example 3, and Comparative Example Awere tested on a Falex extreme pressure wear test apparatus. This testis used to evaluate the load carry capacity of an oil under high contactpressure conditions. The samples were top-treated to the basestock aboveat 0.20 to 0.25 weight percent treatment. These formulated test oilswere not pre-aged. The Falex tests were conducted at room temperature,under 400 pounds load and rotation of the pin at 290 rotations perminute for one hour following a break-in period of 5 minutes at 250pounds load. Test results, shown as weight loss of the pin at the end ofthe test, or as seizure if the parts welded prior to the end of thetest, are in Table 4. The top-treatment of both the comparative exampleA and the product of Example 2 improved the load capacity of thebaseline such that seizure did not occur. TABLE 4 Falex Test ResultsTreat rate, Seizure SAMPLE % S basis (Yes/No) Wt Loss (mg) Basestock 0%Y n/a (baseline) Example 2¹ 0.060 N 35 Example 3¹ 0.039 Y n/aComparative 0.054 N 18.5 Example A¹

Example 7 Gear Test

[0085] The products of Examples 1,2, and 3 and comparative Examples Aand B were tested on an FZG gear test rig modified for “shock load”conditions according to the procedure described by B. -R Hohn et al inScuffing load capacity test in the FZG gear test rigfor gear lubricantswith high EP performance, presented at the Fifth CEC InternationalSymposium on the Performance Evaluation of Automotive Fuels andLubricants 13-15 May, 1997, in Gotegorg Sweden. The FZG “Shock Load”Gear Test was performed to evaluate the antiscuffing properties of thecompounds of this invention. The products of Examples 1 through 3 andtwo commercially available sulfurized isobutylenes, Comparative ExampleA and Comparative Example B. The FZG Gear Test employed the additive at0.9% sulfur in Chevron 600 neutral oil. ASTM D 5182 details the standardprocedure and equipment for the FZG Load Stage test. In the shock loadmethod, the gears were loaded in stages, starting with load stage 1,until 10 mm of a gear tooth surface are scuffed. Table 5 contains thetest results, shown as the stage at which this failure occurred. TABLE 5FZG “shock load” gear test TEST RESULT - Stage at SAMPLE which failureoccurred Example 1 11 Example 2 11 Example 3 8 Comparative Example A 11Comparative Example B 11

[0086] The products of Examples 1 and 2 gave performance comparable tothe commercially available sulfurized isobutylenes.

Example 8 Rear Differential Axel Test

[0087] The L-42 Rear Differential Axel test was performed to evaluatethe compounds of this invention employed in gear lubricant formulations.The products of Examples 1 through 3, Comparative Examples A through Bwere tested for anti-scoring properties under high speed and shockconditions using DANA model 44 hypoid rear axle by the L42 methoddescribed in ASTM publication STP 512A. Test results, in Table 6, arethe scored area on the pinion and ring gears and a pass/fail based oncomparison to a reference oil fonnulation. Samples were tested atvarious concentrations based on sulfur content for the lowestconcentration of the commercial products to pass. The pass/fail criteriarequires that there be less quantity of scoring on the ring and piniongears than on the associated pass reference oil test. To pass,Comparative Example A required a sufficient amount of additive toprovide 1.1% sulfur. At this concentration of sulfur the compositions ofExample 1 and Example 3 did not perform as well as the reference oil.However, it is contemplated that at concentrations of sulfur greaterthan 1.1 and less than 1.8 the compositions of Examples 1 and 3 wouldpass.

[0088] A second test was preformed using the lowest amount of acommercially available product Comparative Example B to pass this test.To pass, Comparative Example B required 1.7% sulfur. As shown from Table6, Example 2 provided superior gear protection at 1.8% sulfur incomparison to Comparative Example B. In fact, at this concentration ofadditive Example 2 a quantity of Scoring Area % data is three timeslower then Comparative Example B. TABLE 6 L42 Test Results Treat rate,Scoring Area % Result SAMPLE % S basis Ring Pinion (Pass/Fail)Comparative 1.1 11 12 Pass Example A Example 1 1.1 27 33 Fail Example 31.2 33 39 Fail Comparative 1.7 14 21 Pass Example B Example 2 1.8 5 6Pass

Example 9 Mini-traction Machine Evaluation

[0089] The products of Example 1 and the product of Example 4 wereevaluated using a PCS Instruments Ltd., London UK, Mini-Traction Machine(MTM) tribometer. The MTM tribometer was set up to run in pin on diskmode using polished disks of 52100 steel from PCS Instruments, and a0.25 inch stationary ball bearing, also of 52100 steel from Falexcorporation, in place of a pin. The test was conducted at 100° C. for 40minutes at 7 Newtons load at a sliding speed of 200 mm/s, following abreak-in period of 5 minutes at 0.1 Newtons and a sliding speed of 2000mm/s. Test results, in Table 7, show the wear scar generated on the ballbearing as measured with an optical microscope by conventional methods.Reported are the average wear scar from 4 test runs. Tests results froma commercially available zinc dithiophosphate are included forcomparison purposes. The product of Example 4 afforded superior wearprotection under the conditions of this test. Product from Example 1 wastested at 3 different concentrations in Chevron 100 neutral oil; productfrom Example 4 was tested at equal sulfur compared to example 1 at 1.9weight %. TABLE 7 MTM test results Wt. % additive in 100 Sample NeutralOil Wear Scar (μm) Example 1 0.5 wt % 575 Example 1 1.0 wt. % 478Example 1 1.9 wt. % 228 Example 4 1.9 wt. % 156 ZnDTP² 1.4 wt. % 172

[0090] As shown from Table 7, the product of Example 4 unexpectedlyyields a superior result compared to ZnDTP in this wear test. This datasuggests that ZnDTP may be replaced by a suitable amount of PDCT in lowphosphorus lubricating oil formulations.

Example 10 Oxidation Test

[0091] Oxidation studies of the product from Example 2 were carried outin a bulk lube oil oxidation bench test as described by E. S. Yamaguchiet al. in Tribology Transactions, Vol.42 (4), 895-901 (1999). In thistest the rate of oxygen uptake by a given volume of oil, with addedmetal catalyst, is monitored at constant pressure and temperature, 171°C. and 2psig 02 for the test results reported in Table 8. The timerequired for 250 ml of oxygen uptake for a 25 g sample, and the time awhich a marked increase in the rate of oxygen uptake was observed, isreported, for a baseline formulation and the baseline formulationtop-treated with 0.5 weight percent of the product of Example 2, in thefollowing table. TABLE 8 Oxidation Test Results Test ParametersFormulation Time, Hrs 250 ml O₂ uptake/25 g Baseline 17.3 Baseline +Example 2 21.7 Increased O₂ uptake Baseline 13.1 Baseline + Example 228.6

What is claimed is:
 1. A composition prepared by sulfurization of ahighly reactive polyisobutylene having at least 25% of amethylvinylidene isomer and wherein the polyisobutylene has a numberaverage molecular weight in the range of about 120 to about 600 with asulfur source at a reaction temperature in excess of about 175° C. 2.The composition according to claim 1 wherein the polyisobutylene moietyis selected from a mixture of C₈H₁₆ to C₃₂H₆₄ oligomers.
 3. Thecomposition according to claim 2 wherein the polyisobutylene comprisesabout 5 wt. % to about 20 wt. % C₈H₁₆, about 35 wt. % to about 55 wt. %C₁₂H₂₄, about 20 wt. % to about 30 wt. % C₁₆H₃₂, about 8 wt. % to about15 wt. % C₂₀H₄₀, about 2 wt. % to about 8 wt. % C₂₄H₄₈, and about 0.5wt. % to about 2 wt. % C₂₈H₅₆ and less than 2 wt% C₃₂H₆₄.
 4. Thecomposition according to claim 1 wherein the reaction is carried out ator below atmospheric pressure.
 5. The composition according to claim 4wherein the polyisobutylene moiety is selected from a mixture of C₁₂H₂₄to C₃₂H₆₄ oligomers.
 6. The composition according to claim 1 wherein thepolyisobutylene moiety has about 40 to 95 % methylvinylidene isomer. 7.The composition according to claim 6 wherein the polyisobutylene moietyhas about 60 to 85 % methylvinylidene isomer.
 8. The compositionaccording to claim 1 wherein the polyisobutylene has a number averagemolecular weight in the range of about 150 to about 240
 9. Thecomposition according to claim 8 wherein the polyisobutylene has anumber average molecular weight in the range of about 175 to about 225.10. A compound of Formula I:

wherein R₁ is hydrogen or methyl; X is sulfur or oxygen; m is an integerfrom 1 to 9; and n is 0 or 1, and when n is 0 then R₁ is methyl, andwhen n is 1 then R₁ is hydrogen.
 11. The compound according to claim 10wherein R₁ is methyl and X is sulfur.
 12. The compound according toclaim 10 wherein R₁ is hydrogen and X is sulfur.
 13. The compoundaccording to claim 10 wherein m is at least
 2. 14. The compoundaccording to claim 10 wherein m is an integer form 1 to
 6. 15. Thecompound according to claim 14 wherein m is an integer from 1 to
 5. 16.A process for preparing a sulfurized olefin composition comprising:reacting a polyisobutylene having at least 25% of a methylvinylideneisomer and wherein the polyisobutylene has a number average molecularweight in the range of about 120 to about 600 with a sulfur source at areaction temperature in excess of 175° C.
 17. The process of claim 16wherein the polyisobutylene moiety is selected from a mixture of C₈H₁₆to C₃₂H₆₄ oligomers.
 18. The process of claim 17 wherein thepolyisobutylene comprises about 5 wt. % to about 20 wt. % C₈H₁₆, about35 wt. % to about 55 wt. % C₁₂H₂₄, about 20 wt. % to about 30 wt. %C₁₆H₃₂, about 8 wt. % to about 15 wt. % C₂₀H₄₀, about 2 wt. % to about 8wt. % C₂₄H₄₈, and about 0.5 wt. % to about 2 wt. % C₂₈H₅₆ and less than2 wt% C₃₂H₆₄.
 19. The process of claim 16 wherein the polyisobutylenemoiety is selected from a mixture of C₁₂H₂₄ to C₃₂H₆₄ oligomers.
 20. Theprocess of claim 16 wherein the polyisobutylene moiety has a least 50 %methylvinylidene isomer.
 21. The process of claim 20 wherein thepolyisobutylene moiety has a least 70 % methylvinylidene isomer.
 22. Theprocess of claim 16 wherein the polyisobutylene has a number averagemolecular weight in the range of about 150 to about 240
 23. The processof claim 22 wherein the polyisobutylene has a number average molecularweight in the range of about 175 to about
 225. 24. The product producedaccording to claim
 16. 25. The product produced according to claim 18.26. A lubricating composition comprising: a. an oil of lubricatingviscosity; b. a sulfurized olefin prepared by reacting a polyisobutylenehaving at least 25% of a methylvinylidene isomer and wherein thepolyisobutylene has a number average molecular weight in the range ofabout 120 to about 600 with a sulfur source at a reaction temperature inexcess of 175° C; c. an ashless dispersant; d. a detergent; e. a metaldialkyl dithiophosphate.
 27. A gear lubricating composition comprising:a. a major amount of oil of lubricating viscosity; b. 0.5 to 8.0 wt. %in terms of sulfur content of a sulfurized olefin prepared by reacting apolyisobutylene having at least 25% of a methylvinylidene isomer andwherein the polyisobutylene has a number average molecular weight in therange of about 120 to about 600 with a sulfur source at a reactiontemperature in excess of 175° C.; c. 0.05 to 5.0 wt. % in terms ofphosphorous content of at least one oil soluble phosphorous containingcompound selected from extreme pressure agents and antiwear agents; d.0.04 to 1.0 wt. % in terms of boron content of an alkali-metal borate orhydrate thereof.
 28. The gear lubricating composition according to claim27 further comprising at least one of the following additionalcomponents: e. 0.1 to 5 wt. % based upon the weight of said lubricationcomposition of at least one ashless dispersant; f. 0.1 to 0.8 wt. %based upon the weight of said lubrication composition of at least onecopper corrosion inhibitor; g. 0.01 to 0.1 wt. % based upon the weightof said lubrication composition of at least one foam inhibitor h. 0.01to 0.1 wt. % % based upon the weight of said lubrication composition ofat least one antirust agent.